搜索结果: 1-15 共查到“知识库 LDPE”相关记录17条 . 查询时间(0.097 秒)
Rheological and mechanical properties of cellulose/LDPE composites using sustainable and fully renewable compatibilisers
blends cellulose and other wood products compatibilization phase behavior rheology
2024/2/29
Cellulose composites with polyethylene (PE) permit to reinforce this commodity polymer, while at the same time introducing renewable content and thus minimizing the use of petroleum-based feedstocks. ...
不同纳米改性LDPE膜对枇杷保鲜效果的影响
纳米改性LDPE膜 枇杷 保鲜效果
2020/3/9
为探讨不同纳米改性低密度聚乙烯(LDPE) 膜对枇杷果实采后保鲜效果的影响,本试验分别研究了普通LDPE膜与纳米改性LDPE膜在室温条件下(20℃)对采后枇杷品质和生理特性的影响。结果表明,与普通LDPE膜相比,纳米Ag、纳米TiO2和纳米SiO2改性LDPE膜可显著抑制采后贮藏过程中枇杷果实的腐烂指数、褐变指数、失重率和硬度的上升及出汁率的下降;延缓其可溶性固形物、可滴定酸和Vc含量的降低;保持...
以废弃瓦楞纸板纤维和低密度聚乙烯(LDPE)为基体辅以相应的相容剂、 润滑剂和发泡剂, 利用挤出发泡法制备了发泡废纸板纤维/LDPE木塑复合材料。通过熔融指数仪研究了废纸板纤维含量、 相容剂马来酸酐接枝聚乙烯(MAH-g-PE)的用量、 润滑剂的种类与用量以及发泡剂偶氮二甲酰胺(AC)的用量对该复合材料加工流变特性的影响; 并利用SEM观察不同熔融指数的复合材料对泡孔形态的影响。结果表明: 随着废...
低温等离子体对低密度聚乙烯(LDPE)薄膜表面改性的研究
有机高分子材料 等离子体处理 低密度聚乙烯 表面改性
2012/3/15
利用低温等离子体, 以氧气为工作气体, 在工作压力为20 Pa、处理功率为30 W的条件下对LDPE薄膜进行了表面改性。用接触角、FTIR--ATR、DSC、SEM、AFM等手段对改性表面进行了分析。结果表明: 在10 s~300 s的处理时间内, 单位面积的失重率随处理时间的增加线性增大; 接触角在0~20 s内随处理时间的增加显著减小, 而在40 s~300 s的处理时间内并没有发生显著变化;...
等离子体处理后UHMWPE纤维与LDPE复合材料的性能
LDPE复合材料 等离子体
2009/10/22
为了改善超高分子量聚乙烯纤维的界面性能,对其进行介质阻挡放电氩等离子体处理以进行表面改性。将等离子处理前后的超高分子量聚乙烯纤维分别与低密度聚乙烯基体制成相同体积比的复合材料,对试样进行纵、横向拉伸性能的测试,探讨经等离子体处理前后复合材料的界面性能。测试结果表明:经氩等离子体处理后纤维的黏合性能得到了较为显著的提高。
考虑结晶潜热的LDPE微结构件注射成型模内温度场
微注射成型 低密度聚乙烯 结晶潜热
2009/8/31
采用含有热源的各向同性物体的热传导处理方法,以及用热焓法处理相变中的结晶潜热问题,建立微注射成型冷却阶段传热过程的数学模型。对结晶型材料低密度聚乙烯(LDPE),在熔体初始温度分别为165, 175和185℃,模温分别为35和55℃时应用有限元软件ANSYS的热分析模块进行仿真分析。研究结果表明:当模温相同而熔体初始温度不同时,熔体温度从熔点温度100℃降到60℃的冷却时间几乎相同;当熔体初始温度...
Breakdown of LDPE Film under Heavy Water Absorption
Low density polyethylene heavy water absorption conduction current
2010/2/2
The breakdown strength characteristic of Low Density
Polyethylene films (LDPE) under DC voltage application and the
effect of water absorption have been studied. Mainly, our experiment
was investig...
The In.uence of Processing Parameters on the Supermolecular Structure of Isotactic Polypropylene in PP/LDPE Blends
isotactic polypropylene polymorphs blends processing
2009/6/16
In order to analyse the effect of the addition of low-density polyethylene (LD-PE) on the
polymorphic transformation in isotactic polypropylene (iPP), structure studies of iPP/LDPE
blends have been ...
X-ray Investigations of the Biodegradation Capacity of PBSA in LDPE/PBSA Blends
Biodegradation Capacity PBSA
2009/6/16
The interdependence between the crystallinity of poly(butylene succinate-co-adipate)
(PBSA) and its biodegradation capacity in blends with low-density polyethylene LDPE has
been studied. The LDPE/PB...
Effects of Washing Solution and LDPE Package on the Quality Changes of Brined Chinese Cabbages at Different Storage Temperatures
brined Chinese cabbage calcium hypochlorite electrolyzed acid-water
2010/2/3
The quality of brined Chinese cabbage after washing (tap water, 100 ppm of calcium hypochlorite, or electrolyzed acid water) followed by package (40 μm or 100 μm LDPE), was investigated at 20, 10, 5, ...
木质素/LDPE-EVA复合材料及其发泡材料的制备
木质素 LDPE-EVA 共混 发泡
2009/1/17
研究了天然可降解高分子材料木质素与LDPE-EVA的共混性能及进一步制备发泡材料的力学性能，共混物SEM图表明，在增容剂LDPE-g-MAH的作用下，木质素均匀地分散于LDPE-EVA基体中，并明显形成了一定的过渡层；DSC曲线分析表明，木质素/LDPE-EVA共混物有且只有一个介于两者吸热峰之间的吸热峰，进一步说明了两者具有较好的相容性。综合看来，10份LDPE-g-MAH增容20份含量的木质素...
多官能单体TMPTA在LDPE表面光接枝聚合研究
光接枝 多官能单体 三羟甲基丙烷三丙烯酸酯（TMPTA）
2008/2/15
以二苯甲酮（BP）为光引发剂、丙酮和水的混合物为溶剂，研究了室温下多官能单体三羟甲基丙烷三丙烯酸酯（TMPTA）在低密度聚乙烯（LDPE）表面的光接枝聚合（＞300nm）.研究表明，多官能单体的接枝速率较快，接枝聚合易产生交联结构，聚合后仍残留双键；延长聚合反应时间、增加单体用量有利于单体接枝转化率的提高；随引发剂用量增加，单体接枝转化率出现一峰值；在研究范围内，混合溶剂中水含量增...
摘要 采用接枝量、ATR－IR、SEM、与水接触角、溶血试验和再钙化时间等测试手段研究了电火花引发甲基丙烯酸β－羟乙酯(HEMA)表面接枝低密度聚乙烯(LAPE)薄膜的接枝聚合反应影响因素、表面结构和血液相容性。结果表明，电火花能有效引发HEMA在LDMA薄膜表面接枝聚合反应，随接枝聚合反应时间延长、单体浓度的增大。接枝量增大。随反应温度升高，接枝量增大到一最大值后，进一步升高反应温度，接枝量下降...
“LDPE土工膜”在绕阳河大堤砂基防渗中的应用
2007/12/13
摘要辽中县绕阳河大堤砂基防渗工程等级标准为2级，文中通过渗流稳定计算分析得出以垂直铺塑法采用“LDPE”土工膜作为防渗材料，并叙述了防渗帷幕的设计及施工过程，防渗效果非常理想。
IUPAC-LDPE的流变性测试实验之间的相对滑动
IUPAC-LDPE熔体 挤出实验 流变性 相对滑动假定 滑动速度
2007/7/28
摘要以IUPAC-LDPE熔体在150oC下详细的流变学表征实验和毛细管挤
出实验为基础考察了该熔体在挤出实验中的滑动问题. 根据相对滑动特性给出了判断相
对滑动存在和计算相对滑动速度的方法. 用Wagner模型, PSM模型和Osaki模型计算的表观
剪切速率, 在10s-1时的毛细管壁面剪切应力比毛细管挤出实验给出的应力值高出
约15%~17%, 这个结果意味着IUPAC-LDPE熔体在挤出实...