Synthesis and luminescence properties of electrodeposited ZnO Films
II-VI semiconductors electrodeposition ZnO photoluminescence thermoelectric electroplating white LED
2011/8/17
Abstract: ZnO films have been grown on gold (111) by electrodeposition using two different OH- sources, nitrate and peroxide, in order to obtain a comparative study between these films. The morphology...
Preparation of ZnO Nanoparticles and Photocatalytic H2 Production Activity from Different Sacrificial Reagent Solutions
Photocatalytic hydrogen production ZnO Photocatalytic activity Sacrificial reagent
2012/4/5
ZnO nanoparticles were synthesized via a direct precipitation method followed by a hetero-geneous azeotropic distillation and calcination processes, and then characterized by X-ray power diffraction, ...
碱土金属添加剂对Cu-ZnO/SiO2催化仲丁醇脱氢反应性能的影响
碱土金属 Cu-ZnO/MgO-SiO2催化剂 仲丁醇 脱氢
2012/11/13
采用碱土金属Mg对SiO2进行预处理后, 用浸渍法制备Cu-ZnO/MgO-SiO2催化剂. 研究不同质量分数Mg对催化剂的结构和性能的影响, 考察该催化剂对仲丁醇脱氢活性和选择性的影响. 采用XRD,TPD和TPR对催化剂进行表征. 实验结果表明, Mg的加入提高了Cu组分的分散度, 同时降低了催化剂表面的酸性. 调节合适的Mg质量分数可获得性能较佳的仲丁醇脱氢催化剂。
ZnO含量对Li2O-ZnO-SiO2玻璃析晶及性能的影响
晶核剂 ZnO Li2O-ZnO-SiO2体系
2012/3/22
应用差示扫描量热仪(DSC)、x-射线衍射(XRD)、扫描电子显微镜(SEM)等分析研究了ZnO含量对Li2O-ZnO-SiO2系玻璃析晶及性能的影响。结果表明,在所研究的微晶玻璃体系中,析出晶相为方石英、磷石英、Li2SiZnO4和SiO2相。随着ZnO添加量的不断增加,析出方石英相相对含量呈现出先增加后减少的趋势。其热膨胀系数α值受析出方石英相相对含量的影响,也呈现出先增加后降低的趋势。当Zn...
以ZnO纳米柱阵列为模板, 采用溶胶-凝胶法制备出TiO2/ZnO和N掺杂TiO2/ZnO的复合纳米管阵列. 扫描电镜(SEM)、X射线光电子能谱(XPS)和紫外-可见漫反射吸收光谱(UV-Vis)的结果表明: 两种阵列的纳米管均为六角形结构, 直径约为100 nm, 壁厚约为20 nm; 在N-TiO2/ZnO复合纳米管阵列中, 掺入的N离子主要是以N-Ox、N-C和N-N的形式化学吸附在纳米管...
共溶剂对ZnO多孔纳米块体孔径均匀性的影响
ZnO纳米颗粒 多孔纳米块体 溶剂热压方法 共溶剂
2010/1/19
以十二烷基硫酸钠(SDS)的水溶液为造孔剂,用溶剂热压方法制备了大孔径的ZnO多孔纳米块体,并进一步考察了添加聚乙二醇400(PEG-400)对样品中孔道的影响. 实验发现,向十二烷基硫酸钠(SDS)的水溶液中加入聚乙二醇400组成共溶剂后, 制备的ZnO多孔纳米块体的孔径大幅度减小,比表面积和孔隙率也明显降低,但孔径的均匀性显著提高.
采用线电爆炸(WEE)方法是在高温、高压的环境中将Zn-Cu合金(w(Zn)=0.65))制备成平均粒径为60-90 nm的Zn-Cu复合纳米颗粒, 在500 ℃焙烧2 h得到纯净的ZnO-CuO纳米复合氧化物. 通过XRD和SEM对ZnO-CuO纳米材料进行分析表征. 以ZnO-CuO纳米复合氧化物为基体材料, 采用传统旁热式结构制成气敏元件, 研究其对C2H5OH的敏感性能. 结果表明, 这种...
ZrO2在Cu-ZnO-ZrO2甲醇水蒸汽重整制氢催化剂中的作用
铜锌锆催化剂 甲醇水蒸汽重整 甲醇 氢气
2010/1/6
通过对一系列Cu-ZnO-ZrO2甲醇水蒸汽重整(SRM)催化剂的XRD、TEM和BET表征及催化性能测定,研究催化剂中ZrO2对催化剂粒径、比表面以及对SRM反应性能的影响.结果表明,ZrO2的加入,使催化剂的粒径从15 nm降至10 nm(其中CuO和ZnO的平均粒径分别从7.7和10.4 nm降至3.9和8.7 nm),BET比表面从60 m2•g-1增至78 m2•...
Development of a ZnO-modified Light-Scattering Sensor for the Detection of Alcohols
a ZnO-modified Light-Scattering Sensor Alcohols
2010/9/20
A light-scattering sensor that incorporated zinc oxide (ZnO) nanoparticles was developed and characterized in this study. Evenly distributed nanostructured ZnO materials were formed on the sensing ele...
溶剂热法制备六角锥形ZnO及其光致发光性能
氧化锌 六角锥形 光致发光性能
2009/12/28
通过乙酸锌和醇溶液反应得到了六角锥形纳米ZnO颗粒, 反应过程中不使用碱溶液和表面活性剂. 利用透射电子显微镜(TEM)、选区电子衍射(SAED)及扫描电子显微镜(SEM)对其形貌和结构进行了表征分析. 结果表明, 此方法制备的ZnO颗粒为单晶, 而且六角锥形ZnO的室温光致发光谱(PL)在378 nm处显示出了单纯的紫外发射峰, 而不是通常报道的可见光区发射, 这也预示着这种特殊结构的纳米ZnO...
以Zn(NO3)2•6H2O和AlCl3•6H2O为原料, 借助CO(NH2)2的水解反应, 采用化学均相共沉淀方法和热处理工艺, 在自制CaSiO3∶Pb, Mn红色荧光粉表面包覆ZnO∶Al, 形成透明导电层. 运用数字万用表和自制测量盒对粉体的电阻率进行测量, 比较了包覆率n(Zn)/n(Ca)、n(Al)/n(Zn), 热处理温度和热处理时间对粉体电阻率的影响; 优...
T-ZnO晶须化学镀铜复合粉体的制备及其电磁性能的研究
T-ZnO晶须 化学镀铜 电磁性能
2009/12/25
采用化学镀的方法制备了Cu包覆四脚状氧化锌晶须(T-ZnO晶须)的复合粉体.使用X射线衍射分析仪(XRD)进行了物象分析,扫描电镜(SEM)观察了粉体的形貌.运用能谱仪(EDS)进行了成份分析.结果表明,晶须为纯氧化锌,晶体结构为六方晶系纤锌矿结构,镀层为纯铜. SEM观察晶须外观形貌为四脚状结构.同时使用波导法对T-ZnO晶须和化学镀铜得到的Cu/T-ZnO晶须复合粉体进行了电磁参数的测量.微...
以混合的锌粉和锡粉作为原料, 通过热蒸发的方法在沉积有金膜的硅基片上制备出具有“芯线-壳层”同轴结构的ZnO/SiOx纳米电缆. 扫描和透射电镜的研究表明, 这种纳米电缆的产量很高, 长度达到数个微米, 并且确认了其“芯线-壳层”的独特结构. 不同于以往ZnO一维纳米材料的三个快速生长方向〈0001〉、〈0110〉及〈2110〉, 其ZnO芯线的生长方向为[2021]. 本实验中锡粉和金膜分别...
采用溶胶-凝胶方法制备ZnO透明溶胶, 在铝箔上涂膜后经500 ℃处理制得具有可见光响应的纳米ZnO薄膜光催化剂. 以甲基橙模拟有机污染物, 在可见光下研究了薄膜的降解性能, 结果表明, 用一片有效面积为200 cm2的ZnO/Al薄膜作为催化剂, 甲基橙的降解率达到96.3%, 比ZnO负载在玻璃上制得的ZnO/glass薄膜催化剂活性高得多. 采用扫描电镜与原子力显微镜对ZnO/Al薄膜制备条...