搜索结果: 1-6 共查到“材料科学 TBC”相关记录6条 . 查询时间(0.059 秒)
Metallographic preparation of the conventional and new TBC layers
Metallic alloys Thin & thick coatings TBC
2009/12/3
Purpose: Verification of up-to-now used metallographic preparation of the TBC coating thermal barriers and adaptation of them to layers of new types, based on new ceramic compounds, sprayed on convent...
Criteria of microstructural assessment of the conventional and new TBC layers
Metallic alloys Thin & thick coatings TBC
2009/12/3
Purpose: The purpose of this paper is to present principles and criteria of microstructural assessment of thermal barrier coatings (TBCs). The conventional layers are described in expert papers, where...
Criteria of assessment of powders provided to spray by the APS method for new and conventional layers type TBC
Metallic alloys Thin&thick coatings TBC
2009/12/3
Purpose: Verification of up-to-now use of conventional powders, provided to spray by the APS method for layers type TBC and its possible adaptation to layers of new types, which are based on new ceram...
Characterisation of APS TBC system during isothermal oxidation at 1100°C
Silesian University of Technology WSK “PZL Rzeszów”
2009/12/1
Purpose: The purpose of presented investigations was metallographical characterization of failure modes of air
plasma sprayed thermal barrier coatings system in isothermal oxidation test conditions a...
Effect of TBC on oxidation behaviour of γ-TiAl based alloy
Metallic alloys Thin & thick coatings TBC Degradation
2010/2/22
Purpose: The purpose of the research was identification of the influence of TBC coating system on oxidation resistance of TiAl based alloy during oxidation at temperature of 900°C and 950°C for 500h a...
Characterisation of air plasma sprayed TBC coating during isothermal oxidation at 1100°C
Thin & thick coatings TBC Degradation Oxidation
2010/2/22
Purpose: The purpose of the research was characterization of failure modes of air plasma sprayed thermal barrier coatings system in isthermal oxidation test conditions at 1100ºC.
Design/methodol...